Modification of SPS quasicrystalline compacts via electron beam treatment
 Poczklán, Ladislav ; Lukáč,, František (referee) ; Čížek, Jan (advisor)
The quasicrystals are characterized by unusual rotational symmetries that are not observed in the crystalline materials, which is the cause of their interesting material properties. Because of that a particular attention was paid to quasicrystalline structures in the literature research. The research also contains a description of electron beam technology, spark plasma sintering method and introduction to the problematics of wear. As the default materials for the experimental part were selected Titanium Grade 2 powder and Cristome A5 powder which was partially composed of quasicrystalline phase. The first series of samples was sintered only from powder Cristome A5. The second series was sintered from the mixture of 80 % Titanium Grade 2 powder and 20 % Cristome A5 powder. For the compaction of samples spark plasma sintering technology was selected. Samples were then systematically modified by electron beam and subjected to pin on disc tests. Samples modified at 750 °C had the best wear resistance. Samples modified at 1150 °C contained increased amount of quasicrystalline phase.
Detailed record
Modification of SPS quasicrystalline compacts via electron beam treatment
 Poczklán, Ladislav ; Lukáč,, František (referee) ; Čížek, Jan (advisor)
The quasicrystals are characterized by unusual rotational symmetries that are not observed in the crystalline materials, which is the cause of their interesting material properties. Because of that a particular attention was paid to quasicrystalline structures in the literature research. The research also contains a description of electron beam technology, spark plasma sintering method and introduction to the problematics of wear. As the default materials for the experimental part were selected Titanium Grade 2 powder and Cristome A5 powder which was partially composed of quasicrystalline phase. The first series of samples was sintered only from powder Cristome A5. The second series was sintered from the mixture of 80 % Titanium Grade 2 powder and 20 % Cristome A5 powder. For the compaction of samples spark plasma sintering technology was selected. Samples were then systematically modified by electron beam and subjected to pin on disc tests. Samples modified at 750 °C had the best wear resistance. Samples modified at 1150 °C contained increased amount of quasicrystalline phase.
Detailed record

Interested in being notified about new results for this query?
Subscribe to the RSS feed.
Digital Repository :: Search :: Submit :: Personalize :: Help
Powered by Invenio v1.1.2
Maintained by admin.invenio@techlib.cz
This site is also available in the following languages:
Česky  English